Introduction
Sintered bronze bearings(bronze powder), made of bronze powder as base material, are produced by the process of being pressed in mold, sintered in high temperature and absorbed oil in vacuum. They are widely used in the applications of automotive, motor cycle, office equipment and electronic tool due to the advantages of good self-lubricating,good wear resistance and stable size.
Chemical Composition%
Material coda/ MPIF standard |
Cu |
Sn |
Zn |
Pb |
graphite |
other |
CT-1000-K19 |
87.2-90.5 |
9.5-10.5 |
/ |
/ |
0-0.3 |
0-2.0 |
CT-1000-K26 |
87.2-90.5 |
9.5-10.5 |
/ |
/ |
0-0.3 |
0-2.0 |
CT-1000-K37 |
87.2-90.5 |
9.5-10.5 |
/ |
/ |
0-0.3 |
0-2.0 |
CT-1000-K40 |
87.2-90.5 |
9.5-10.5 |
/ |
/ |
0-0.3 |
0-2.0 |
CTG-1001-K17 |
85.7-90.0 |
9.5-10.5 |
/ |
/ |
0.5-1.8 |
0-2.0 |
CTG-1001-K23 |
85.7-90.0 |
9.5-10.5 |
/ |
/ |
0.5-1.8 |
0-2.0 |
CTG-1001-K30 |
85.7-90.0 |
9.5-10.5 |
/ |
/ |
0.5-1.8 |
0-2.0 |
CTG-1001-K34 |
85.7-90.0 |
9.5-10.5 |
/ |
/ |
0.5-1.8 |
0-2.0 |
CTG-1004-K10 |
82.8-88.3 |
9.2-10.2 |
/ |
/ |
2.5-5.0 |
0-2.0 |
CTG-1004-K15 |
82.8-88.3 |
9.2-10.2 |
/ |
/ |
2.5-5.0 |
0-2.0 |
Physical Properties
Material coda/ MPIF standard |
Strength Coefficient |
|||
103psi |
Mpa |
Oil content % |
Density (g/cm3) |
|
CT-1000-K19 |
19 |
130 |
24 |
6.0-6.4 |
CT-1000-K26 |
26 |
180 |
19 |
6.4-6.8 |
CT-1000-K37 |
37 |
260 |
12 |
6.8-7.2 |
CT-1000-K40 |
40 |
280 |
9 |
7.2-7.6 |
CTG-1001-K17 |
17 |
120 |
22 |
6.0-6.4 |
CTG-1001-K23 |
23 |
160 |
17 |
6.4-6.8 |
CTG-1001-K30 |
30 |
210 |
9 |
6.8-7.2 |
CTG-1001-K34 |
34 |
230 |
7 |
7.2-7.6 |
CTG-1004-K10 |
10 |
70 |
11 |
5.8-6.2 |
CTG-1004-K15 |
15 |
100 |
0-10 |
6.2-6.6 |